Polymer-bitumen rapes, heat shrink tapes

Polymer-bitumen rapes are to be used for wrapping the coating during en route capital repairs of the insulation coating (re-insulation) of gas pipelines with a diameter of up to 1420 mm inclusive and a transported product temperature of +35 °Ñ maximum.
Ratio, measurement unit Standard as per Technical Specifications
LITKOR-NK-GAZPOLYKOR

DONRAD-GAZ, DONRAD-ARM

POLYLEN-OB
Plasticity on a beam, rounding radius = 10 mm, °Ñ, maximum -20 -20 -20 -
Adhesion to bitumen-polymer  coating, t= 20°Ñ, N/cm, minimum 10,0 10,0 10,0 -
Adhesion of overlapped tapes, t = 20°Ñ, N/cm, minimum 7,0 7,0 7,0 >7,0
Resistance of base tape rupture lengthwise, t = +23±2°Ñ, MPa, minimum 12,0 12,0 - -

Heat shrink tapes are to be used as a protective wrap for combined coatings based on bitumen-polymer mastics to protect main, infield and process pipelines. The tapes are rollsproduced by the extrusion method and are subject to relaxation (length shrinks) at 60 °Ñ.

Ratio, measurement unitStandard as per Technical Specifications
TERMA-LDRL-LPOLYTHERM
Rupture resistance, MPa, minimum 12 12 >12
Relative rupture elongation, %, minimal 200 200 >200
Electric strength, kW/mm, minimum 10 5 -
Lengthwise shrinkage, %, minimal at t = 140 °Ñ 15 15-40 15-30
Relaxation, %, minimal at t = 60 °Ñ 4 3-10 >4

 

 

© 2011 CJSC “Gazprom StroyTEK Salavat”

6, Prospekt Vernadskogo, Moscow,
Business Centre Capitol.

Location map and detailed information

 The content and design of the website includes materials from gazprom.ru